Paslanmaz Kimyasal kompozisyonları
|
AISI Amerikan |
Fab No |
C % Max |
Cr % |
Ni % |
Mo % |
Mn % Max |
P % Max |
S % Max |
Si % |
Diğer |
|
304 |
1.4301 |
0.08 |
18-20 |
8-11 |
|
2.00 |
0.045 |
0.030 |
1.00 |
|
|
|
1.4306 |
0.03 |
18-20 |
8-13 |
|
2.00 |
0.045 |
0.030 |
1.00 |
|
|
316 |
1.4401 |
0.08 |
16-18 |
11-14 |
2.00-3.0 |
2.00 |
0.045 |
0.030 |
1.00 |
|
|
|
1.4404 |
0.03 |
16-18 |
10-14 |
2.00-3.00 |
2.00 |
0.045 |
0.030 |
1.00 |
|
|
316
Ti |
1.4571 |
0.08 |
16-18 |
10-14 |
2.00-3.000 |
2.00 |
0.045 |
0.030 |
1.00 |
Ti
= 5x%C min |
|
321 |
1.4541 |
0.08 |
17-20 |
9-12 |
|
2.00 |
0.045 |
0.030 |
1.00 |
Ti
= 5x%C min |
|
310 |
1.4841 |
0.20 |
24-26 |
19-22 |
|
2.00 |
0.045 |
0.030 |
1.50 |
|
|
310 S |
1.4845 |
0.08 |
24-26 |
19-22 |
|
2.00 |
0.045 |
0.030 |
0.75 |
|
|
430 |
1.4016 |
0.12 |
16-18 |
0.50 max |
|
1.00 |
0.040 |
0.030 |
0.75 |
|
|
430 Ti |
1.4510 |
0.10 |
16-19.5 |
0.75 max |
|
1.00 |
0.040 |
0.030 |
1.00 |
Ti = 5x%C min, 0.75 max |
|
409 |
1.4512 |
0.08 |
10.5-12 |
0.50 max |
|
1.00 |
0.045 |
0.045 |
1.00 |
Ti
= 6x%C min, 0.75 max |
|
DIN Alman |
DIN İtalyan |
AISI USA |
AFNOR Fransız |
BSI İngiliz |
JIS Japon |
SIS İsveç |
|
1.4301 |
X5CrNi 18 8 |
304 |
Z6CN 18-09 |
304 S 31 |
SUS 304 |
2332 |
|
1.4306 |
X2CrNi 18 8 |
|
Z2CN 19-10 |
304 S 12 |
SCS 19 |
2352 |
|
1.4401 |
X5CrNiMo 17 12 2 |
316 |
Z6CND 17-11 |
316 S 16 |
SUS 316 |
2347 |
|
1.4404 |
X2CrNiMo 17 13 2 |
|
Z2CND 17-12 |
316 S 14 |
SUS |
2348 |
|
1.4571 |
X6CrNiMoTi 17 12 2 |
316 Ti |
Z6CNDT 17-12 |
320 S 31 |
|
2350 |
|
1.4541 |
X6CrNiTi 18 8 |
321 |
Z6CNT 18-10 |
321 S 12 |
SUS 321 |
2337 |
|
1.4841 |
X15CrNiSi 25 20 |
310 |
Z12CNS 25-20 |
|
SUH 310 |
|
|
1.4845 |
X12CrNi 25 21 |
310 S |
Z12CN 25-20 |
310 S 24 |
SUS 310 S |
2361 |
|
1.4016 |
X6Cr 17 |
430 |
Z8C 17 |
430 S 15 |
SUS 430 |
2320 |
|
1.4510 |
X6CrTi 17 |
430 Ti |
Z8CT 17 |
|
SUS 430 LX |
|
|
1.4512 |
X6CrTi 12 |
409 |
Z6CT 12 |
409 S 17 |
SUH 409 |
|